REGITEX MG Series
	The REGITEX MG Series is natural rubber latex which has been modified by graft polymerization of MMA (Methyl Methacrylate). Depending on the grafting ratio, we have MG-10, MG-25, MG-40 and MG-67, which demonstrate superior functions as the raw material for various adhesives and latex modifiers.
	Application Examples
	Base material for adhesives for leather shoes Used widely as the base material for heat resistant lasting adhesives and adhesives for uncured rubber tape Base material of adhesives for textiles Utilized particularly where flexibility is demanded PVC adhesive tape Used in the base material for the primers to prevent plasticizer migration, and in the adhesive layer Adhesive for flocking Has excellent adhesive properties with respect to cooking gloves, cured rubber for flocking glue and textiles Modifier for dipped latex products By adding 5 to 10% sulfur cured latex, hardness is increased and rubber degradation is effectively prevented Modifiers of latex and emulsion based adhesives Effective in modifying the physical adhesive properties by adjusting the amount added to match the application Base material for the adhesives for rubber particles for work gloves Rubber particles have high compound stability and excellent adhesion Binder for leather board and pulp board Excellent as a binding agent on its own, and even as a base material for binding agents it has favorable compound stability Binder for tyre chips Favorable as a coloring agent for tyre chip surfaces Base material for adhesives in paper processing Is used as the base material for cold sealing agents and resealable adhesives Base material for primers used principally for the purpose of increasing the adhesion of rubber material Used by masticating and dissolving in organic solvents.
	MG Series List
	Latex Characteristics MG-10S MG-25 MG-40S MG-67 Viscosity (B type, mPa.s) 60 30 40 30 pH 10 10 10 10 Total Solids (%) 50 51 51 51
	Physical performance
	Physical Properties MG-10 MG-25 MG-40S MG-67 Modulus 100% (MPa) 0.6 1.1 1.8 2.3 Modulus 300% (MPa) 0.7 1.5 2.8 3.4 Modulus 600% (MPa) 1.8 5.8 9.9 11.7 Tensile Strength (MPa) 16.5 30.0 23.5 24.5 Stretch (%) 1000 850 720 680 Conditions for fabrication of the test membrane: 1. Film casting on glass, 2. Drying (room temperature, 1 day), 3. Heat treatment (90)